Characteristics of the complex modulus of recycled cold mix with foamed bitumen and recycled concrete aggregate

Type: paper published in a journal

Author

Title variant

Polish

Charakterystyka modułu zespolonego mieszanki mineralno-cementowej z asfaltem spienionym i destruktem z betonu cementowego

Publication date

2019

Published in

MATEC Web of Conferences

Vol.

262

Abstract

English

This article presents research on recycled cold mix with foamed bitumen (MCAS) containing recycled concrete aggregate. The primary concept driving this research was to determine if recycled concrete aggregate (RC) could be used as a substitute for reclaimed asphalt pavement (RAP). Recycled concrete aggregate was used in the MCAS mix in amounts ranging from 20%, 60% and 80%. The reference mix was the MCAS mix containing 50% reclaimed asphalt pavement (RAP) and virgin aggregate. Identical 0/31.5-mm continuously graded dolomite virgin aggregate was used in all mixes. 2.5% foamed bitumen (FB) and 2.0% CEM I 42.5R Portland cement (PC) were used to increase the cohesion of the mineral mix. Foamed bitumen was produced from 50/70 penetration paving bitumen. The behaviour of the recycled base course was tested in the range of cyclic sinusoidal strain with amplitude εo = 25–50 με. The tests were carried out in the (-7°C, 5°C, 13°C, 25°C, 40°C) temperature and (0.1 Hz, 0.3 Hz, 1 Hz, 3 Hz, 10 Hz, 20 Hz) loading time range. The complex modulus was tested in a direct tension-compression test on cylindrical samples (DTC-CY) in accordance with EN 12697-26. The results of the tests were used to assess the complex modulus (E*), phase angle (φ) and complex modulus components (E1) and (E2).Tests of the mixes indicate that recycled concrete aggregate can be used in recycled cold mixes in amounts of up to 80%. Increasing the amount of recycled concrete aggregate does not cause excessive stiffness of the recycled mix in comparison with the reference mix. The tests did not demonstrate a significant difference in terms of the phase angle (φ), which indicates a similar content of the viscous part and elastic part in the obtained complex modulus for the reference mix (RAP + MCAS) and the mix containing recycled concrete aggregate (RC + MCAS).

Keywords